FloTube™ 6101 CP120-6A10 PA66 MB 10%
- Chemical Family
- Carbon Fiber
FloTube™ 6101 CP120-6A10 PA66 MB 10% contains 10% 6101FloTube™ carbon nanotubes with a smooth surface and good dispersion in the masterbatch.
Properties
- Physical Form
- Masterbatch
- Solid
Product families
Applications
Applications
- Consumer Goods — Sports & Recreation
Automotive & Transportation — Automotive
- Fuel Systems
- Tires
Electrical & Electronics — Parts & Components
- Batteries
Product Families
Elastomers — Elastomer Additives
- Performance Additives
- Surface Modifiers
Plastics — Masterbatches
- Additive Masterbatches
Plastics — Polymer Additives
- Performance Additives
- Surface Modifiers
Other characteristics
- Brand
- FloTube
- Carrier
- Polyamide 66 (PA 66), Resin-based
- Polyamide 66 (PA 66)
- Resin-based
- Functions
- Anti-Static Agent, Conductive Agent
- Processing Methods
- Injection Molding
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Elastomers
- Plastics
- Material Features
- Good Dispersion
- Smooth Surface Finish
- Plastics and Elastomers End Uses
- Batteries
- Sporting Goods
- Tires
- Plastics and Elastomers Functions
- Anti-Static Agent
- Conductive Agent
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Break | 75.0 | MPa | ASTM D638 |
| Tensile Elongation at Break | 4.0 | % | ASTM D638 |
| Flexural Strength | 126.0 | MPa | ASTM D790 |
| Flexural Modulus | 2900.0 | MPa | ASTM D790 |
| Impact Strength, Izod Notched | 65.0 | J/m | ASTM D256 |
Table 2 of 4
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Relative Density 23/23°C | 1.16 | — | ASTM D792 |
| Mold Shrinkage | 1.8 | % | ASTM D955 |
| Melt Flow Rate at 275 ° C, 5 Kg | 26.1 | g/ 10min | ASTM D1238 |
| Tensile Strength | 75 | MPa | ASTM D638 |
| Tensile Elongation | 4 | % | ASTM D638 |
| Flexural Strength | 126 | MPa | ASTM D79D |
| Flexural Modulus | 2900 | MPa | ASTM D79D |
| Impact Strength. Izod Notched | 65 | J/m | ASTM D256 |
| Volume Resistivity | 1000000-10000000 | Ohm*cm | ESD STM 11.12 |
| Surface Resistivity | 1000000-10000000 | Ohm/ sq. | ESD STM 11.11 |
Table 3 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistance | 2022-10-10 | Ω.cm | ESD STM 11.12 |
| Surface Resistivity (Injection Molding) | 106-107 | Ω/sq. | ESD STM 11.11 |
Table 4 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Relative density (23/23°C) | 1.16 | — | ASTM D792 |
| Mold Shrinkage | 1.8 | % | ASTM D955 |
| Melt Flow lIndex (250°C / 2.16Kg) | 26.1 | g/10min | ASTM D1238 |