GLS Polymers PPCP FR V0
- Chemical Family
- PolyolefinsPolypropylenes (PP)
GLS Polymers PPCP FR V0 is Filled With Flame Retardant.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Other Industrial Applications
- Tooling & Moldmaking
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Polymer Name
- Polypropylene Copolymer
- Melt Flow Index
- 8.0 - 8.0 g/10 min
- Processing Methods
- Injection Molding
- Markets
- Industrial
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Material Features
- Flame Retardant
- Certifications and Compliance
- RoHS Compliant
- UL 94
- Plastics and Elastomers End Uses
- Mold Making
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 4
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Impact Strength, Izod notched 1/8 in (3.2 mm) section | 60 - 85 | J/m | D 256 |
| Tensile Strength | 22 - 26 | MPa | D 638 |
| Tensile Elongation at Yield | min. 10 | % | D 638 |
| Flexural Strength | 20 - 25 | MPa | D 790 |
| Flexural Modulus | 1200 - 1500 | MPa | D 790 |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature at 264 psi (1820 kPa) | 50 – 55 | °C | D 648 |
| Flammability as per UL 94 3.0mm | V0 | — | UL 94 |
Table 3 of 4
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 0.85 - 1.25 | — | D 792 |
| Melt Flow Rate at 230 °C, / 2.16 kg | min. 8 | g/10 min | D 1238 |
| Molding Shrinkage 3.2 mmsection | 1.2 –1.8 | % | D955 |
Table 4 of 4
4 rows| Characteristic | Value | Unit |
|---|---|---|
| Injection Pressure | 65 -105 | MPa |
| Melt Temperature | 190 - 220 | °C |
| Mold Temperature | 32-64 | °C |
| Drying at 78°C | 2 | hr |