SCIGRIP® SG5000-13
- Chemical Family
- Methacrylates
SCIGRIP® SG5000-13 Methacrylate Adhesives are high strength two-component products for bonding metals2 , plastics1 and composites. They offer a unique combination of convenient 1:1 mix ratio and ability to adhere to a wide variety of materials. Most metals, including steel and aluminum, can be bonded without surface pretreatment. A choice of 3, 6 and 15 minute working times, fast cure and rapid strength build make this series of adhesives an ideal first choice for diverse bonding applications. Packaging options include 50 and 400 ml cartridges and in 19 and 189 liters (5 and 50 gallon) bulk containers for application with meter-mix dispense equipment.
Product families
- Other Adhesives & Sealants
Other characteristics
- Brand
- SCIGRIP
- Product Type
- 2K (2 component) Adhesive
- Compatible Substrates & Surfaces
- Aluminum, Composites, Metal, Steel
- Curing
Working time is the approximate time, after mixing components A and B that the adhesive remains fluid and bondable. Fixture time is the approximate time after mixing components A and B required for the adhesive to develop sufficient strength to allow careful movement, unclamping or de-molding of assembled parts. Parts can generally be put in service when 80 percent of full strength is developed. The time to achieve 80% cure is approximately 2-3 times that required for fixturing. The working and fixture times presented in this bulletin are based on laboratory tests performed at 75°F (24°C). Higher temperatures speed the curing reaction, which reduces working time and speeds the development of strength. The reverse is true for lower temperatures. If significant variation in temperatures or application at very high or low temperatures is anticipated, contact your SCIGRIP representative for technical assistance.
- Safety
Read Material Safety Data Sheet before handling or using this product. Adhesive component A contains flammable methyl methacrylate monomer. Always use in a well-ventilated area. Floor-level extraction and large quantities of moving air greatly facilitate ventilation. Activator component B contains peroxide. Both materials must be stored in a cool place away from sources of heat and open flames or sparks. Keep containers closed when not in use. Prevent contact with skin and eyes. In case of skin contact, wash with soap and water. In case of eye contact, flush with water for 15 minutes and seek immediate medical attention. Harmful if swallowed. Keep out of reach of children.
- Markets
- Adhesives & Sealants
- Clean Up
Adhesive components and mixed adhesive should be removed from mixing and application equipment with a suitable industrial solvent or cleaner before the mixed adhesive cures. Once the adhesive cures, soaking in a strong solvent or paint remover will be required to soften the adhesive for removal. If the bonds are exposed to UV rays then use of plasticizers such as Benzoflex 2088 is recommended, or contact your SCIGRIP representative for additional information. Any clean-up of the bonded assembly using industrial solvents is not recommended as it could affect the cure.
- Applications
Adhesives & Sealants — Other Adhesives & Sealants Applications
- Technology
- Ready-to-Use Products
- Packaging Type
- Bulk
- Cartridges
- Performance Benefits
• Primerless metal bonding for most metals - Eliminates surface treatment steps • Choice of 3, 6 and 15 minute working times - Selection to fit process requirements • Non critical 1:1 mix ratio - Excellent results with manual or metered mixing • Excellent environmental & chemical resistance - Permanent bonds in harsh environments • Minimal surface preparation - Offers clean shop and speedy assembly process
Technical data
Table 1 of 1
5 rows| Characteristic | Value | Unit |
|---|---|---|
| Tensile Strength (24°C) | 35-40 (5,076-5,802) | psi (MPa) |
| Maximum Tensile Elongation (24°C) | 2021-05-10 | % |
| Tensile Modulus (24°C) | 1,100-1,240 (160,000-180,000) | psi (MPa) |
| Lap Shear Strength (24°C) | 18-25 (2,611-3,626) | psi (MPa) |
| Service Temperatures (24°C) | -40-212 | °C |