TCI Powder Coatings OGF Epoxy Hybrid Primer (7820-12396)
- Chemical Family
- Epoxy & Epoxy Derivatives
TCI Powder Coatings OGF Epoxy Hybrid Primer (7820-12396) is an epoxy coating formulated to provide excellent chemical and corrosion resistance, as well as good properties such as adhesion and flexibility. It is ideally suited for interior applications or as a primer. Reduce cure schedule to 5min at 375F if followed by powder top coat. Fully cure as indicated if used with liquid top coat. Pre-test with intended top coat to validate production conditions.
Product families
- Powder Coatings
- Primers & Sealers
Other characteristics
- Features
Chemical Resistant, Corrosion Resistant, Excellent Substrate Adhesion, Good Barrier Properties, Good Flexibility, High Hardness
- Product Type
Epoxy Coating, Hybrid Coating, Powder Coating, Primer; Epoxy Coating; Hybrid Coating; Powder Coating; Primer
- Markets
- Paints & Coatings
- Storage
TCI recommends storage below 80 °F and 60% RH. All stock materials should be used in FIFO order (first in/first out). Products that have exceeded the recommended shelf life should be tested before use.
- Shelf LIfe
- 12 months
- Applications
Paints & Coatings — Other Paints & Coatings Applications
- Key Features
- Epoxy system
- Ideally suited for interior applications
- Excellent hardness, flexibility, and adhesion
- Excellent corrosion and chemical resistance
- Technology
- Ready-to-Use Products
- Environmental Testing
Substrate Preparation: Substrate should be free of all organic and inorganic dirt, oil and/or contaminants. Chemical conversion coatings are highly recommended to ensure maximum protection and film longevity. A primer is recommended when finished products are exposed to extreme corrosive environments.
- Certifications and Compliance
- ISO 9001
- Ready to Use Product Features
- Chemical Resistant
- Corrosion Resistant
- Excellent Substrate Adhesion
- Good Barrier Properties
- Good Flexibility
- High Hardness
Technical data
Table 1 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Pencil Hardness | H-2H | — | ASTM D3363 |
| Flexibility | 2021-01-08 | in. | ASTM D522 |
| Direct Impact | 40.0 | in.-lb. | ASTM D2794 |
| Reverse Impact | 40.0 | in.-lb. | ASTM D2794 |
Table 2 of 2
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.67 +/- 0.05 | — | ASTM D5965 |
| Theoretical Coverage | 115.3 | sq. ft./lb/mil | — |
| Particle Size Distribution | 85 - 100 | microns | D90 |
| Film Thickness | 2.0 - 3.0 | mils | — |
| 60° Gloss | 70 - 89 | — | — |
| Cure Schedule (Metal Temperature, 375 °F) | 10.0 | minutes | — |